Cement Floor Heating Module Mold Adhesive
InquiryThe cement floor heating module mold adhesive is a condensation-type liquid silicone produced with a formulation ratio of 100 parts silicone to 2 parts curing agent. This product is made from high-quality raw materials, specifically designed to address the challenges posed by heavier cement products, which can easily damage molds. It is particularly suitable for creating cement underfloor heating modules, ensuring that intricate patterns are reproduced with precision and clarity. This innovative silicone rubber effectively overcomes the limitations of other materials that struggle to replicate the intricate designs found on cement surfaces.
Technical Parameters
| Product Name | Cement Floor Heating Module Mold Adhesive | |||||
| Catalog | ALOS-SILI-229 | ALOS-SILI-230 | ALOS-SILI-231 | ALOS-SILI-232 | ALOS-SILI-233 | ALOS-SILI-234 |
| Color | Semi-transparent or white | Semi-transparent or white | Semi-transparent or white | Semi-transparent or white | Semi-transparent or white | Semi-transparent or white |
| Hardness | 15±2 HSA | 20±2 HSA | 25±2 HSA | 30±2 HSA | 33±2 HSA | 40±2 HSA |
| Viscosity | 13000±2000 mPa·s | 17000±2000 mPa·s | 25000±2000 mPa·s | 27000±2000 mPa·s | 25000±2000 mPa·s | 15000±2000 mPa·s |
| Vulcanizer Addition Amount | 2-3% | 2-3% | 2-3% | 2-3% | 2-3% | 2-3% |
| Tensile Strength | 2.5 MPa | 2.8 MPa | 3.4 MPa | 4.0 MPa | 4.0 MPa | 3.5 MPa |
| Tear Strength | 16±2 kN/m | 19±2 kN/m | 24±2 kN/m | 25±2 kN/m | 25±2 kN/m | 21±2 kN/m |
| Elongation | 380% | 530% | 410% | 420% | 450% | 180% |
| Density | 1.08g/ cm3 | 1.08g/ cm3 | 1.08g/ cm3 | 1.08g/ cm3 | 1.09g/ cm3 | 1.09g/ cm3 |
| Operation Time | 30-50 min | 30-50 min | 30-40 min | 30-40 min | 30-40 min | 30-50 min |
| Vulcanization Time | 4-5 h | 4-5 h | 3-4 h | 3-4 h | 3-4 h | 4-5 h |
| Linear Shrinkage | 0.3% | 0.3% | 0.3% | 0.3% | 0.3% | 0.3% |
Features
- The cement floor heating module mold adhesives feature excellent fluidity, making them easy to work with and simple to release from the mold. This enhances the efficiency and convenience of the molding process.
- With high tear strength and impressive tensile properties, these cement floor heating module mold adhesives can endure multiple demolding cycles, making them suitable for repeated use in various applications.
- With a low shrinkage rate, this adhesive cures rapidly at room temperature, enabling efficient and timely production.
- These cement floor heating module mold adhesives are versatile, making them suitable for the replication of various products—whether large, medium, or small—and for manufacturing silicone molds with complex shapes.
Operation Steps
- Begin by meticulously mixing silicone rubber with the curing agent in a specific ratio, ensuring that the mixture is homogeneous. This step is crucial for achieving optimal results in the mold-making process.
- Once the silicone mixture is thoroughly combined, it must be vacuumed to remove bubbles. Failing to do so can lead to imperfections in the mold, resulting in air pockets that may compromise its quality.
- After preparing the mold, apply a release agent to both the mold and the mold frame. Secure the mold in the center of the frame, and then carefully pour the de-aired silicone mixture into the frame until it fully covers the mold. Allow the silicone to sit undisturbed, permitting it to cure completely.
- Once the silicone has fully cured, proceed to demold it carefully. After demolding, address any rough edges to achieve a smooth finish.