Silicone Pad Printing Adhesive

Inquiry

At Alfa Chemistry, we offer two types of silicone pad printing adhesives: addition type pad printing adhesives and condensation type pad printing adhesives. These high-performance, eco-friendly, and non-toxic adhesives are made from organic silicone rubber, featuring moderate viscosity that facilitates easy dispensing. Notably, the curing process is exotherm-free, without the release of low molecular weight byproducts, resulting in minimal shrinkage and deep curing capabilities. Once cured, the silicone exhibits a fine texture and excellent resiliency, ensuring that printed patterns are sharp and clear. Moreover, these adhesives provide outstanding ink transfer performance, making them an ideal choice for various applications.

Addition Type Pad Printing Adhesives Technical Parameters

Product Name	Addition Type Pad Printing Adhesives
Catalog	Color	Curing Agent Addition Amount	Curing Time	Curing Condition	Hardness	Viscosity	Operation Time	Tensile Strength	Tear Strength	Elongation	Linear Shrinkage
ALOS-SILI-237	Green	10%	4-6 h	Room temperature/high temperature	33±2 HSA	70000±10% mPa·s	30-60 min	6 MPa	25 kN/m	310%	1.5%
ALOS-SILI-238	Red	10%	4-6 h	Room temperature/high temperature	33±2 HSA	70000±10% mPa·s	30-60 min	6 MPa	25 kN/m	310%	1.5%

Condensation Type Pad Printing Adhesives Technical Parameters

Product Name	Condensation Type Pad Printing Adhesives
Catalog	Color	Curing Agent Addition Amount	Curing Time	Curing Condition	Hardness	Viscosity	Operation Time	Tensile Strength	Tear Strength	Elongation	Linear Shrinkage
ALOS-SILI-239	White	2%	3-4 h	Room temperature	25±2 HSA	28000±10% mPa·s	8-15 min	3 MPa	15 kN/m	280%	2%
ALOS-SILI-240	Yellow	2%	3-4 h	Room temperature	25±2 HSA	50000±10% mPa·s	8-15 min	3 MPa	15 kN/m	280%	2%
ALOS-SILI-241	Red	2%	3-4 h	Room temperature	25±2 HSA	30000±10% mPa·s	8-15 min	3 MPa	15 kN/m	300%	2%
ALOS-SILI-242	Red	2%	3-4 h	Room temperature	25±2 HSA	32000±10% mPa·s	8-15 min	3 MPa	16 kN/m	330%	2%
ALOS-SILI-243	Yellow	2%	3-4 h	Room temperature	25±2 HSA	50000±10% mPa·s	8-15 min	3 MPa	15 kN/m	300%	2%
ALOS-SILI-244	Red	2%	3-4 h	Room temperature	25±2 HSA	30000±10% mPa·s	8-15 min	3 MPa	18 kN/m	330%	2%
ALOS-SILI-245	Gray	2.5%	2-3 h	Room temperature	25±2 HSA	22000±10% mPa·s	8-15 min	2 MPa	5 kN/m	200%	2%
ALOS-SILI-246	Gray	2%	3-4 h	Room temperature	25±2 HSA	32000±10% mPa·s	8-15 min	2.2 MPa	8 kN/m	230%	2%
ALOS-SILI-247	Off-white	2%	2-3 h	Room temperature	25±2 HSA	22000±10% mPa·s	8-15 min	2 MPa	5 kN/m	200%	2%
ALOS-SILI-248	White	2%	3-4 h	Room temperature	25±2 HSA	28000±10% mPa·s	8-15 min	3 MPa	18 kN/m	300%	2%
ALOS-SILI-249	White	2%	2-3 h	Room temperature	25±2 HSA	20000±10% mPa·s	8-15 min	3 MPa	20 kN/m	380%	2%
ALOS-SILI-250	Yellow	2%	2-3 h	Room temperature	25±2 HSA	30000±10% mPa·s	8-15 min	3 MPa	20 kN/m	380%	2%
ALOS-SILI-251	Yellow	2%	3-4 h	Room temperature	25±2 HSA	50000±10% mPa·s	8-15 min	3 MPa	18 kN/m	280%	2%
ALOS-SILI-252	Yellow	2%	3-4 h	Room temperature	25±2 HSA	50000±10% mPa·s	8-15 min	3 MPa	18 kN/m	280%	2%
ALOS-SILI-253	Red	2%	3-4 h	Room temperature	22±2 HSA	30000±10% mPa·s	8-15 min	3 MPa	18 kN/m	280%	2%
ALOS-SILI-254	White	2%	3-4 h	Room temperature	25±2 HSA	32000±10% mPa·s	8-15 min	3 MPa	16 kN/m	350%	2%
ALOS-SILI-255	Yellow	2%	3-4 h	Room temperature	25±2 HSA	50000±10% mPa·s	8-15 min	3 MPa	15 kN/m	350%	2%
ALOS-SILI-256	Gray yellow	2.5%	3-4 h	Room temperature	31±2 HSA	32000±10% mPa·s	15-25 min	2MPa	8 kN/m	230%	2%
ALOS-SILI-257	Red	2%	3-4 h	Room temperature	25±2 HSA	30000±10% mPa·s	8-15 min	3 MPa	16 kN/m	350%	2%
ALOS-SILI-258	Yellow	2.5%	3-4 h	Room temperature	31±2 HSA	32000±10% mPa·s	15-25 min	2 MPa	8 kN/m	230%	2%
ALOS-SILI-259	Red	2.5%	3-4 h	Room temperature	31±2 HSA	32000±10% mPa·s	15-25 min	2 MPa	8 kN/m	230%	2%
ALOS-SILI-260	Yellow	2.5%	3-4 h	Room temperature	30±2 HSA	32000±10% mPa·s	15-25 min	2 MPa	8 kN/m	250%	2%
ALOS-SILI-261	Red	10%	3-4 h	Room temperature	27±2 HSA	30000±10% mPa·s	15-25 min	3 MPa	22 kN/m	400%	2%
ALOS-SILI-262	Yellow	2.5%	3-4 h	Room temperature	30±2 HSA	32000±10% mPa·s	15-25 min	2 MPa	8 kN/m	230%	2%
ALOS-SILI-263	White	2.5%	3-4 h	Room temperature	30±2 HSA	32000±10% mPa·s	15-25 min	2 MPa	8 kN/m	230%	2%